The flexural strength of 3D-printed provisional restorations fabricated with different resins: a systematic review and meta-analysis

BMC Oral Health volume 24, Article number: 66 (2024) Cite this article

Abstract

Background

Three-dimensional (3D) printing technology has revolutionized dentistry, particularly in fabricating provisional restorations. This systematic review and meta-analysis aimed to thoroughly evaluate the flexural strength of provisional restorations produced using 3D printing while considering the impact of different resin materials.

Methods

A systematic search was conducted across major databases (ScienceDirect, PubMed, Web of Sciences, Google Scholar, and Scopus) to identify relevant studies published to date. The inclusion criteria included studies evaluating the flexural strength of 3D-printed provisional restorations using different resins. Data extraction and quality assessment were performed using the CONSORT scale, and a meta-analysis was conducted using RevMan 5.4 to pool results.

Results

Of the 1914 initially identified research articles, only 13, published between January 2016 and November 2023, were included after screening. Notably, Digital Light Processing (DLP) has emerged as the predominant 3D printing technique, while stereolithography (SLA), Fused Deposition Modeling (FDM), and mono-liquid crystal displays (LCD) have also been recognized. Various printed resins have been utilized in different techniques, including acrylic, composite resins, and methacrylate oligomer-based materials. Regarding flexural strength, polymerization played a pivotal role for resins used in 3D or conventional/milled resins, revealing significant variations in the study. For instance, SLA-3D and DLP Acrylate photopolymers displayed distinct strengths, along with DLP bisacrylic, milled PMMA, and conventional PMMA. The subsequent meta-analysis indicated a significant difference in flexure strength, with a pooled Mean Difference (MD) of − 1.25 (95% CI − 16.98 - 14.47; P < 0.00001) and a high I2 value of 99%, highlighting substantial heterogeneity among the studies.

Conclusions

This study provides a comprehensive overview of the flexural strength of 3D-printed provisional restorations fabricated using different resins. However, further research is recommended to explore additional factors influencing flexural strength and refine the recommendations for enhancing the performance of 3D-printed provisional restorations in clinical applications.

Peer Review reports

Background

The use of three-dimensional (3D)-printed temporary dental restorations is increasing in clinical settings owing to the widespread availability of intraoral scanning technology, user-friendly dental computer-aided design (CAD) software, and rapid 3D printing capabilities [1]. Recently, it has gained significant attention in the field of dentistry. It has revolutionized dental restorations, including provisional restorations [2, 3]. Utilizing technology in dental prosthesis production is more advantageous than traditional methods, such as the lost-wax technique, owing to material and energy conservation benefits, reduced carbon emissions, and cost-effectiveness [4]. Moreover, Provisional restorations rely on factors such as flexural strength to ensure that abutment teeth remain stable during the interim period [5], and they offer temporary support, protection, and aesthetics until the final restorations are made [6].

Flexural strength is the material’s resistance to bending without breaking, which is crucial for dental restorations, as it ensures that they withstand forces during mastication [7]. 3D printing technology facilitates the creation of temporary restorations using various resins, each with distinct compositions, curing procedures, and physical characteristics. These variations may influence the flexural strength of provisional restorations [8].. By evaluating the flexural strength, dental professionals can ensure the durability and longevity of restorations [9]. This assessment guides materials and fabrication techniques for optimal performance and patient satisfaction. Moreover, understanding the factors affecting flexural strength improves the design and production of 3D-printed provisional restorations, thereby enhancing clinical success rates [10].

Therefore, assessing flexural strength is crucial for evidence-based decision-making and guiding future advancements in restorative dental care. Understanding the flexural strength of 3D-printed provisional restorations using different resin materials is essential. This enables dental practitioners to make informed decisions when selecting materials with the desired mechanical properties [11]. This knowledge can help optimize the choice of resins for specific clinical scenarios, considering factors such as anticipated functional loads and occlusal forces.

Using various resins in the 3D printing of temporary restorations provides versatile possibilities and benefits [12, 13]. These temporary restorations are vital in dental practice and serve as provisional substitutes when permanent restorations are fabricated [14]. Different resins, such as methacrylate-based and photopolymerizable resins, exhibit unique properties that can be tailored to specific clinical requirements [15]. These resins differ in their mechanical strength, esthetics, biocompatibility, and ease of manipulation [16]. One important consideration when selecting resins is their flexural strength [17]. Choosing a resin with optimal flexural strength is crucial for temporary restorations to withstand occlusal forces and prevent fractures or debonding [18]. Additionally, Esthetic properties, such as color and clarity resembling natural teeth, are crucial for visually pleasing outcomes, which can enhance esthetics and patient satisfaction during the interim period [19]. Choosing biocompatible resins for temporary restorations is vital to avoid adverse reactions or complications, especially in patients who may be sensitive or allergic to specific materials [20, 21]. Efficient manipulation and rapid curing of dental materials are crucial. Quick-curing resins streamline dental workflows and reduce chairside time, improving patient comfort.

Moreover, DIN EN ISO 6872:2019 is a reference for biaxial flexural strength testing; however, additional measures are required to ensure the consistency and comparability of results across different laboratories [22]. In addition, adherence to the fabrication guidelines outlined in ISO 20795.1:2013 and ASTM D790 is recommended [23].

Conducting a systematic study and meta-analysis of the flexural strength of 3D-printed provisional restorations made from various resins is imperative for a thorough understanding of their performance and longevity. With the increasing use of 3D printing technology in dentistry, understanding the effects of different resin materials on the flexural strength of provisional restorations is crucial for clinicians and researchers. This research can aid in making informed decisions regarding material selection and treatment planning, ultimately improving the quality and longevity of dental restorations while enhancing patient care and satisfaction. Thus, the present study was designed to critically analyze and summarize the existing literature on the flexural strength of 3D-printed provisional restorations fabricated using different resins.

Methods

This systematic review and meta-analysis adhered to the guidelines outlined by the Preferred Reporting Items for Systematic Reviews and Meta-Analysis (PRISMA) criteria [24]. The protocol used for this systematic review was the registered international platform for registered systematic reviews and meta-analysis protocols (INPLASY) (2023110054).

Literature search

The search strategy was established according to the participants, intervention, comparators or controls, and outcome (PICO) framework [25]. Population/Participants: 3D printed provisional. Intervention: Types of resins affecting strength. Comparison or control: temporary restorations/denture bases. Outcomes: Effect of various factors on Flexural Strength. Different databases such as ScienceDirect, Web of Sciences, PubMed, GoogleScholar, and Scopus were searched using different keywords and Medical subject heading terms (MeSH) terms along with Boolean operators such as “Flexural strength [Mesh Term]” OR “Flexural” OR “Strength,” “Resistance,” “Printing, three dimensional [MeSH Term]” OR “3D printing”, “3D printing”, “CAD materials,” “Provisional restorations,” “Temporary restorations,” Interim restorations,” “Transitional restorations,“ Substitute restorations,” “Resin materials,” “polymer resins,” “Photopolymers,” “Methacrylate-based resins,” “Photopolymerizable resins,” “Ionomer” (Supplementary Table 1).

Inclusion criteria

Studies that provided data on the flexural strength of provisional restorations made using 3D printing techniques employing various resin materials were considered. In vitro experiments, comparative studies, and clinical trials were eligible for inclusion, regardless of their location or setting. The selected studies were expected to present clear and relevant information, including the mean flexural strength values, standard deviations, and type of 3D printing technology employed. Additionally, studies incorporating resins with varying chemical compositions or characteristics, such as biocompatibility and esthetic properties, were included for comprehensive analysis and comparison. Randomized controlled trials (RCTs) and prospective or comparative studies published in peer-reviewed journals between 2013 and 2023 were included.

Exclusion criteria

Studies lacking pertinent data on flexural strength, those not published in peer-reviewed journals, and those not presented in English were excluded. Additionally, studies involving non-human subjects or those that exclusively focused on permanent restorations rather than provisional restorations were excluded. Case series, case reports, observational studies, and reviews.

Study selection and assessment

Original publications, study titles, and abstracts were independently evaluated. Two reviewers independently assessed the entire text of the papers that met the inclusion requirements, and their conclusions were discussed to arrive at a consensus. Any disagreements were resolved by a third independent reviewer and settled by consensus.

Data extraction

Information retrieval was performed for the selected studies that met the inclusion criteria. After screening the papers’ titles, abstracts, and full texts, a data extraction form was used to record the extracted data. Two reviewers independently recorded each demographic characteristic (study author details, country, experimental design, and sample size), 3D Printing Parameters (printed type, risen type, layer thickness, wavelength/light intensity, temperature settings, and build orientation), control, testing method for strength, post-processing or treatment applied, conclusion, and limitations for a systematic review. The mean flexural strength values and their corresponding standard deviations are essential for statistical analysis in a meta-analysis and for constructing forest plots.

Quality assessment

Given that all selected studies were in vitro investigations, their quality was evaluated using the CONSORT scale with 14 items (Appendix 1) for in vitro studies [26, 27].

Data analysis

This systematic review incorporated articles through qualitative analysis. The PRISMA checklist served as the framework for systematically reviewing relevant literature, and a systematic step-by-step approach was employed to select articles. Additionally, the meta-analysis phase was conducted using RevMan 5.4 [28] to calculate the Cochrane Q and I2 values, quantifying trial dispersion. A random-effects model was used, with the significance level set at 0.05.

Results

Literature searched

An exhaustive review of the scientific literature was conducted using multiple electronic databases. All the identified research articles were published in highly esteemed peer-reviewed journals. Following stringent analysis, 1914 relevant articles were identified. Subsequently, 281 duplicate articles were identified and excluded. The remaining 1633 publications underwent a meticulous examination of their titles and abstracts, which revealed that 1594 articles were not pertinent to the scope of our study and were consequently excluded. Subsequently, the remaining 39 articles were subjected to comprehensive scrutiny, resulting in the removal of 26 articles for various reasons (Fig. 1). Tables 1 and 2 have been included to provide a detailed overview of the 13 remaining studies published between January 2016 and November 2023, highlighting their essential characteristics and features.

Fig. 1
figure 1

PRISMA flow chart

Full size image
Table 1 Demographic and 3D printer characteristics of the included studies
Full size table
Table 2 Summary of the outcomes related to flexure strength
Full size table

General characteristics

The studies included in the analysis were conducted in a range of countries. Most studies were conducted in South Korea [1, 29, 30] and Brazil [31,32,33], followed by Saudi Arabia [34, 35], China [36], Turkey [37], Romania [38], India [39], and Germany [40]. Most studies have employed Digital Light Processing (DLP) [30, 33, 35, 38, 40], stereolithography (SLA) [32], Both DLP and SLA [1, 29, 34], Fused Deposition Modeling (FDM) [1], and mono-liquid Crystal Display (LCD) [36], with a variety of printed materials, such as acrylic, composite resin, and methacrylate oligomer-based materials. The layer thickness was 50 μm in most studies [30, 34, 35, 40], and the wavelength/light intensity varied across studies, with a maximum of 405 nm/13.14 mW/cm 2[34]. The temperature settings, build orientation, and post-curing times were addressed differently (Table 1). The control materials included polymethyl methacrylate (PMMA), heat-activated polymerized Polymethyl methacrylate (PMMA) resin, self-cured resin, heat-polymerized acrylic, milled materials, acrylic resin, zirconia crowns, conventional auto-polymerized resin, conventional pressure/heat-cured acrylic resin, and various composite resins (Table 1).

Outcomes

The study outcomes (Table 2) encompassed a comprehensive analysis of the various testing methods employed to evaluate the flexural strength of the dental materials and their respective strength values (Table 2). The most commonly used testing methods include the 3-point flexural bend test [31,32,33,34,35,36,37,38], universal testing machine [1, 29, 30, 39], and piston-on-three-ball (P3B) method [40]. Polymerization leads to flexural strengths of PR = 79.54, CH = 95.58, and CC = 104.20 [39]. In the case of the SLA-3D technique and DLP Acrylate photopolymer, flexure strengths were recorded as 116.08 and 46.83, respectively, while DLP Bis-acrylic and Milled PMMA exhibited strengths of 146.37 and 168.57, respectively, and Conventional PMMA registered 89.54 [29]. Notably, the FDM group did not experience any breakage. For values exceeding 50 MPa, post-polymerization treatment was applied to NextDent (56.4 MPa) and the control (93.4 MPa) [36]. Graphy exhibited a flexural strength of 329.3, whereas NextDent measured 177.8, with no specific treatment [30]. The flexural strengths of 3DCS, 3DOS, CHP, and CAP were 143, 141, 76, and 88, respectively [38], and they underwent polymerization. When post-polymerization was conducted with 3000 flashes of ultraviolet light, the cosmos temperature was 56.83, Evolux PMMA was 111.76, and Structur 2 SC was 87.34 [32]. Moreover, the flexural strength results before accelerated aging (pre-aging) showed that the A2 group had a significantly greater strength of 151 ± 7 MPa (p < 0.05) than the other groups following the polishing and aging procedures [35]. The flexural strengths of the 3D polymer-infiltrated ceramic network and nanohybrid composite resin were 83.5, 140.3, and 237.3, respectively [40]. Most studies reported that the study design was a limitation (Table 2).

Meta-analysis

Nine studies with 785 samples in the intervention (3D printed) and control groups (resin used in conventional or milled techniques) were included to assess the flexural strength of 3D-printed provisional restorations fabricated with different resins. As shown in Fig. 2, our pooled result found a significant difference in flexure strength, with a pooled Mean Difference (MD) of − 1.25 (95% CI − 16.98 - 14.47; P < 0.00001) and I2 = 99%.

Fig. 2
figure 2

Forest plot for flexure strength

Full size image

Quality assessment

All studies (13) included the abstract, introduction, intervention, outcome, statistical method, and results (Items 1–4, 10, and 11) [1, 29,30,31,32,33,34,35,36,37,38,39,40]. While 12 studies delved into the limitations of the trials (Item 12), nine disclosed information about their funding sources (Item 13) [1, 30,31,32,33,34,35,36,37,38,39,40]. Interestingly, none of the studies addressed sample size calculation for the specimens (Item 5) or accessibility of the full trial protocol (Item 14). Additionally, there was a notable absence of information regarding the method used to generate a random allocation sequence (item 6) in any of the studies. Furthermore, none of the studies provided details regarding the blinding of the examiners or information about the researcher responsible for generating the random allocation (Items 8 and 9), as outlined in Table 3.

Table 3 Quality assessment of In-vitro studies
Full size table

Discussion

The flexural strength of 3D-printed provisional restorations is critical for assessing their structural integrity and suitability for clinical use [41]. As digital technologies continue to reshape the landscape of prosthodontics, the choice of printing materials plays a pivotal role in determining the mechanical performance of the final restorations [42]. This study investigated the flexural strength of 3D-printed provisional restorations, focusing on the influence of different resin materials. By scrutinizing the mechanical properties of these restorations, we aimed to provide valuable insights that can inform clinicians and researchers about the comparative strengths associated with various resin options, ultimately guiding informed decision-making in the realm of digitally fabricated provisional prosthetics.

In the present study, DLP was the most commonly used 3D technique, which may be due to its efficiency, speed, and high-resolution capabilities [43]. In dental applications, where precision and quick turnaround times are paramount, DLP technology excels by utilizing a digital light source to selectively cure all layers of liquid resin simultaneously [44]. This simultaneous curing accelerates the printing process compared to other methods, such as LCD 3D, SLA, or FDM [45]. In addition, DLP printers often provide a higher resolution, enabling the production of intricately detailed dental structures with exceptional accuracy [46]. The ability to rapidly produce precise, high-quality dental models and prosthetics has positioned DLP as the preferred choice, streamlining the workflow in dental laboratories and clinics [46]. Meanwhile, a statistically significant difference in trueness was observed when comparing the LCD 3D printer and DLP 3D printers (p = 0.004). Similarly, for precision, a statistically significant difference was found between the LCD 3D printer and DLP 3D printers (p = 0.011), indicating that the DLP 3D printer exhibited greater accuracy in dental model printing than the LCD 3D printer [47]. Similarly, no statistically significant differences were observed among the four software types analyzed using the DLP printer. Nevertheless, a group comprising the amalgamation of D-CAD (Blender–InLAB) exhibited the highest average (− 0.0324 SD = 0.0456), demonstrating superior accuracy compared to the group with the lowest average (consisting of the Meshmixer and Blender models), which included generic and specific software (0.1024 SD = 0.0819) [48]. Furthermore, DLP printers showed a notable advantage over LCD printers in another study, displaying lower RMS values and less shrinkage in 5-unit and full-arch cases. Point deviation analysis revealed significant directional differences in all DLP-printed restorations. However, only a few LCD printing and DLP printer cases have proven to be the most accurate for short-unit restorations, demonstrating reduced deviation and shrinkage [49]. In contrast, the DLP and FDM groups observed significant differences in trueness and precision. The average trueness values for DLP and FDM were 0.096 (0.021) (P < 0.001) and 0.063 mm (0.024) (P < 0.001), respectively. Similarly, the average precisions for DLP and FDM were 0.027 mm (0.003) (P < 0.001) and 0.036 mm (0.003) (P < 0.001), respectively. Notably, widening (0.158 mm [0.089] for DLP and 0.093 mm [0.005] for FDM, P = 0.05) and twisting (0.03 mm [0.014] for DLP and 0.043 mm [0.029] for FDM, P = 0.05) of the printed models were observed. FDM demonstrated greater accuracy, suggesting its suitability as a viable alternative to DLP [50].

Moreover, various printed materials, such as acrylic, composite resin, and methacrylate oligomer-based materials, have been identified. These diverse substances cater to different applications and offer a range of properties, including strength, flexibility, and biocompatibility. Acrylic polymers, known for their durability and versatility, are commonly utilized in 3D printing because of their adaptability to various applications [51]. Composite resins blend different materials for enhanced characteristics, balanced strength, and aesthetics, making them suitable for dental and aesthetic applications [52]. With their unique chemical compositions, methacrylate oligomer-based materials contribute to developing materials with specific properties often used to synthesize resins optimized for 3D printing processes [53]. The utilization of these materials underscores the flexibility of 3D printing technologies in accommodating a wide array of applications and functional requirements.

Polymerization plays a crucial role in determining the flexural strengths of different materials, and notable variations were observed in this study. For instance, SLA-3D and DLP Acrylate photopolymers exhibited distinct strengths, as did DLP bisacrylic, milled PMMA, and conventional PMMA. These diverse findings underscore the complex interplay of material composition, printing techniques, and post-processing treatments in determining flexural strength (Table 2). The question arises as to why polymerization plays a vital role because it is a chemical process by which monomers, the building blocks of polymers, join together to form a larger, more complex structure. In 3D printing, this process is fundamental for creating solid and durable objects from liquid or semi-liquid resin materials [54]. The resin transforms from a liquid or semi-liquid state to a solid state during polymerization, creating a three-dimensional network of polymer chains. The polymerization process’s extent and efficiency directly affect the printed object’s final mechanical properties, including its flexural strength [55, 56]. Incomplete polymerization can result in structural weaknesses, reduced bond strength between polymer chains, and compromised mechanical properties. In contrast, well-controlled and thorough polymerization contributed to forming a robust and homogenous material, enhancing its flexural strength. As shown in Table 2, the different resin materials used in the 3D printers underwent polymerization. This underscores the significance of the polymerization process in influencing the mechanical properties, particularly the flexural strength of 3D-printed resin materials [57]. Similarly, in another study, 40 resin samples were mechanically tested using a universal testing machine, with subsequent fractographic analysis of the failed bending samples. Additively manufactured samples demonstrated higher elastic moduli (2.4 ± 0.02 GPa and 2.6 ± 0.18 GPa) and average bending strength (141 ± 17 MPa and 143 ± 15 MPa) compared to conventional samples (1.3 ± 0.19 GPa and 1.3 ± 0.38 GPa for elastic moduli; 88 ± 10 MPa and 76 ± 7 MPa for bending strength). The results indicated greater homogeneity in the materials produced through additive manufacturing [38]. In contrast, different materials were polymerized in another study, and the flexural strength, including cold-polymerized PMMA, recorded 125.90 MPa for heat-polymerized PMMA, 140 MPa for auto-polymerized bis-acryl composite (133 MPa), and light-polymerized urethane dimethacrylate resin measured 80.84 MPa. Notably, the highest flexural strength was observed for heat-polymerized PMMA. The lightly polymerized urethane dimethacrylate resin exhibited the lowest flexural strength, indicating a significant difference in strength between the materials [5].

The meta-analysis in the present study indicated a statistically significant difference in flexure strength between the groups (MD = − 1.25, 95% CI: − 16.98 - 14.47, p < 0.00001). An I2 value of 99% suggested high heterogeneity among the included studies, indicating substantial variability in effect sizes. A negative mean difference shows reduced flexure strength in the experimental group compared to the control group. This may be due to differences in the characteristics of the compared groups, diverse methodologies for assessing flexural strength, and disparities in the types of materials or 3D printing technologies employed. The sample size and geographic location might have also contributed to the observed heterogeneity. Our findings align with those of other studies, and milling techniques demonstrated notably higher flexural strength values (Hedge g = − 3.88; 95% CI, − 7.20 to − 0.58; P = 0.02), and this difference persisted even after the aging process (Hedge g = − 3.29; 95% CI, − 6.41 to − 0.17; P = 0.04) compared to printing [58]. Similarly, the milled resin exhibited mechanical properties in flexure strength that were superior or comparable to those of the bisacrylic resin. In contrast, 3D-printed resins demonstrate statistically inferior properties compared to milled and bisacrylic resins [32]. In contrast, one study indicated that printed samples exhibited higher mean bending strengths (141 ± 17 and 143 ± 15 MPa) than traditional samples (88 ± 10 and 76 ± 7 MPa). These findings suggest superior mechanical properties in terms of elastic moduli and bending strength for printed samples and imply a higher degree of homogeneity in the material when produced through printing processes [38]. The mean flexural strengths for CAD/CAM, injection molding, and compression molding were 97.46, 84.42, and 71.72, respectively, with corresponding standard deviations of 9.93, 10.42, and 11.58, respectively. Statistical analysis indicated that CAD/CAM is the optimal denture fabrication method, exhibiting the highest mean flexural strength and lowest standard deviation compared to compression and injection molding [59].

Although this study offers valuable insights, its strengths and limitations should be acknowledged. The strength lies in the comprehensive synthesis of existing literature, which provides a collective understanding of the flexural strength across various 3D printing resins. Meta-analysis adds quantitative rigor to the findings, thus enhancing their statistical robustness. However, the limitations include potential heterogeneity among the included studies arising from variations in methodologies, printing technologies, and materials. Reliance on available published data may introduce publication bias, and the dynamic nature of 3D printing technologies may result in temporal discrepancies. Despite these limitations, this study is valuable for clinicians, researchers, and industry professionals seeking evidence-based insights into the flexural strength of 3D-printed provisional restorations.

Conclusions

This systematic review and meta-analysis comprehensively examined the flexural strength of 3D-printed provisional restorations crafted using diverse resins. The pooled results revealed a significant difference in the flexural strength between the studied resin materials, emphasizing careful consideration when selecting materials for provisional restorations. Notably, the heterogeneity observed in the meta-analysis underscores the variability in methodologies and material characteristics across the included studies. However, the negative mean difference suggests a lower flexural strength in certain experimental groups than in the controls. Further research and subgroup analyses are imperative to unravel the sources of heterogeneity and refine our understanding of the nuanced factors influencing the flexural strength of 3D-printed provisional restorations with different resin compositions.

Availability of data and materials

The data supporting this study’s findings are available from the corresponding author upon reasonable request.

Abbreviations

3D:

Three-dimensional

DLP:

Digital Light Processing

SLA:

Stereolithography

FDM:

Fused Deposition Modeling

LCD:

Liquid Crystal Display

MD:

Mean difference

CAD:

Computer-aided design

RCTs:

Randomized controlled trials

PMMA:

Polymethyl methacrylate

P3B:

Piston-on-three-ball method

References

  1. Park S-M, Park J-M, Kim S-K, Heo S-J, Koak J-Y. Flexural strength of 3D-printing resin materials for provisional fixed dental prostheses. Materials. 2020;13(18):3970.

    Article  PubMed  PubMed Central  Google Scholar 

  2. Dobrzański LA, Dobrzański LB. Dentistry 4.0 concept in the design and manufacturing of prosthetic dental restorations. Processes. 2020;8(5):525.

    Article  Google Scholar 

  3. Punia U, Kaushik A, Garg RK, Chhabra D, Sharma A. 3D printable biomaterials for dental restoration: a systematic review. Mater Today: Proceed. 2022;63:566–72.

    Google Scholar 

  4. Ishida Y, Miyasaka T. Dimensional accuracy of dental casting patterns created by 3D printers. Dent Mater J. 2016;35(2):250–6.

    Article  PubMed  Google Scholar 

  5. Idrissi HA, Annamma LM, Sharaf D, Jaghsi AA, Abutayyem H. Comparative evaluation of flexural strength of four different types of provisional restoration materials: an in vitro pilot study. Children. 2023;10(2):380.

    Article  PubMed  PubMed Central  Google Scholar 

  6. Patras M, Naka O, Doukoudakis S, Pissiotis A. Management of provisional restorations' deficiencies: a literature review. J Esthetic Restorat Dentist. 2012;24(1):26–38.

    Article  Google Scholar 

  7. Ilie N, Hilton T, Heintze S, Hickel R, Watts D, Silikas N, Stansbury J, Cadenaro M, Ferracane J. Academy of dental materials guidance—resin composites: part I—mechanical properties. Dent Mater. 2017;33(8):880–94.

    Article  PubMed  Google Scholar 

  8. Tahayeri A, Morgan M, Fugolin AP, Bompolaki D, Athirasala A, Pfeifer CS, Ferracane JL, Bertassoni LE. 3D printed versus conventionally cured provisional crown and bridge dental materials. Dent Mater. 2018;34(2):192–200.

    Article  PubMed  Google Scholar 

  9. Yanıkoğlu ND, Sakarya RE. Test methods used in the evaluation of the structure features of the restorative materials: a literature review. J Mater Res Technol. 2020;9(5):9720–34.

    Article  Google Scholar 

  10. Fernandes NA, Vally Z, Sykes LM. The longevity of restorations-a literature review. South African Dental J. 2015;70(9):410–3.

    Google Scholar 

  11. Soto-Montero J, de Castro EF, Romano BD, Nima G, Shimokawa CA, Giannini M. Color alterations, flexural strength, and microhardness of 3D printed resins for fixed provisional restoration using different post-curing times. Dent Mater. 2022;38(8):1271–82.

    Article  PubMed  Google Scholar 

  12. Della BA, Cantelli V, Britto VT, Collares KF, Stansbury JW. 3D printing restorative materials using a stereolithographic technique: a systematic review. Dent Mater. 2021;37(2):336–50.

    Article  Google Scholar 

  13. Alshadidi AAF, Alshahrani AA, Aldosari LIN, Chaturvedi S, Saini RS, Hassan SAB, Cicciù M, Minervini G. Investigation on the application of artificial intelligence in prosthodontics. Appl Sci. 2023;13(8):5004.

    Article  Google Scholar 

  14. Burns DR, Beck DA, Nelson SK. A review of selected dental literature on contemporary provisional fixed prosthodontic treatment: report of the committee on research in fixed prosthodontics of the academy of fixed prosthodontics. J Prosthet Dent. 2003;90(5):474–97.

    Article  PubMed  Google Scholar 

  15. Hata K, Ikeda H, Nagamatsu Y, Masaki C, Hosokawa R, Shimizu H. Development of dental poly (methyl methacrylate)-based resin for stereolithography additive manufacturing. Polymers. 2021;13(24):4435.

    Article  PubMed  PubMed Central  Google Scholar 

  16. Da Silva TM, Immich F, De Araujo TS, Lund RG, Da Silva AF, Piva E, Da Rosa WLDO. Photosensitive resins used in additive manufacturing for oral application in dentistry: a scoping review from lab to clinic. J Mech Behav Biomed Mater. 2023;105732

  17. Gömeç Y, Dörter C, Dabanoglu A, Koray F. Effect of resin-based material combination on the compressive and the flexural strength. J Oral Rehabil. 2005;32(2):122–7.

    Article  PubMed  Google Scholar 

  18. Yazigi C, Kern M, Chaar MS. Influence of various bonding techniques on the fracture strength of thin CAD/CAM-fabricated occlusal glass-ceramic veneers. J Mech Behav Biomed Mater. 2017;75:504–11.

    Article  PubMed  Google Scholar 

  19. Ye Z, Jiang J, Yang L, Xu T, Lin Y, Luo F. Research Progress and clinical application of all-ceramic Micro-veneer. Materials. 2023;16(8):2957.

    Article  PubMed  PubMed Central  Google Scholar 

  20. Schmalz G. Determination of Biocompatibility. In: Schmalz G, Berlin A-BD, editors. Biocompatibility of Dental Materials. Berlin Heidelberg: Heidelberg: Springer; 2009. p. 13–43.

    Chapter  Google Scholar 

  21. Nair S, Madhav VNV, Saini RS, Alshadidi AAF, Aldosari LIN, Heboyan A. 28Assessment of thermal variations in the pulpal chamber during fabrication of provisionals using two different techniques and three materials. Technol Health Care. 2023. https://0-doi-org.brum.beds.ac.uk/10.3233/THC-230933. Epub ahead of print.

  22. Spintzyk S, Geis-Gerstorfer J, Bourauel C, Keilig L, Lohbauer U, Brune A, Greuling A, Arnold C, Rues S, Adjiski R, et al. Biaxial flexural strength of zirconia: a round robin test with 12 laboratories. Dent Mater. 2021;37(2):284–95.

    Article  PubMed  Google Scholar 

  23. Chander NG, Jayaraman V, Sriram V. Comparison of ISO and ASTM standards in determining the flexural strength of denture base resin. Eur Oral Res. 2019;53(3):137–40.

    Article  PubMed  PubMed Central  Google Scholar 

  24. Page MJ, Moher D, McKenzie JE. Introduction to PRISMA 2020 and implications for research synthesis methodologists. Res Synth Methods. 2022;13(2):156–63.

    Article  PubMed  Google Scholar 

  25. Schardt C, Adams MB, Owens T, Keitz S, Fontelo P. Utilization of the PICO framework to improve searching PubMed for clinical questions. BMC Med Inform Decis Making. 2007;7(1):16.

    Article  Google Scholar 

  26. Faggion CM Jr. Guidelines for reporting pre-clinical in vitro studies on dental materials. J evidence-based dental pract. 2012;12(4):182–9.

    Article  Google Scholar 

  27. Krithikadatta J, Gopikrishna V, Datta M. CRIS guidelines (checklist for reporting in-vitro studies): a concept note on the need for standardized guidelines for improving quality and transparency in reporting in-vitro studies in experimental dental research. J conservat dentistry : JCD. 2014;17(4):301–4.

    Article  Google Scholar 

  28. Higgins JP, Thomas J, Chandler J, Cumpston M, Li T, Page MJ, Welch VA. Cochrane handbook for systematic reviews of interventions. John Wiley & Sons; 2019.

    Book  Google Scholar 

  29. Cho W-T, Choi J-W. Comparison analysis of fracture load and flexural strength of provisional restorative resins fabricated by different methods. J Korean Academ Prosthodont. 2019;57(3):225–31.

    Article  Google Scholar 

  30. Kim N, Kim H, Kim I-H, Lee J, Lee KE, Lee H-S, Kim J-H, Song JS, Shin Y. Novel 3D printed resin crowns for primary molars: in vitro study of fracture resistance, biaxial flexural strength, and dynamic mechanical analysis. Children. 2022;9(10):1445.

    Article  PubMed  PubMed Central  Google Scholar 

  31. Simoneti DM, Pereira-Cenci T, Dos Santos MBF. Comparison of material properties and biofilm formation in interim single crowns obtained by 3D printing and conventional methods. J Prosthet Dent. 2022;127(1):168–72.

    Article  PubMed  Google Scholar 

  32. Souza ALC, Cruvinel Filho JL, Rocha SS. Flexural strength and Vickers hardness of milled and 3D-printed resins for provisional dental restorations. Brazil J Oral Sci. 2023;22:e238439–9.

    Article  Google Scholar 

  33. Ribeiro AKC, de Freitas RFCP, de Carvalho IHG, de Miranda LM, da Silva NR, de Fátima Dantas de Almeida L, Zhang Y, da Fonte Porto Carreiro A, de Assunção E Souza RO: Flexural strength, surface roughness, micro-CT analysis, and microbiological adhesion of a 3D-printed temporary crown material. Clin Oral Investig. 2023, 27(5):2207–2220.

    Article  PubMed  Google Scholar 

  34. Al-Qarni FD, Gad MM. Printing accuracy and flexural properties of different 3D-printed denture base resins. Materials. 2022;15(7):2410.

    Article  PubMed  PubMed Central  Google Scholar 

  35. Alageel O, Alhijji S, Alsadon O, Alsarani M, Gomawi AA, Alhotan A. Trueness, flexural strength, and surface properties of various three-dimensional (3D) printed interim restorative materials after accelerated aging. Polymers. 2023;15(14):3040.

    Article  PubMed  PubMed Central  Google Scholar 

  36. Chen H, Cheng D-H, Huang S-C, Lin Y-M. Comparison of flexural properties and cytotoxicity of interim materials printed from mono-LCD and DLP 3D printers. J Prosthet Dent. 2021;126(5):703–8.

    Article  PubMed  Google Scholar 

  37. Taşın S, Ismatullaev A. Comparative evaluation of the effect of thermocycling on the mechanical properties of conventionally polymerized, CAD-CAM milled, and 3D-printed interim materials. J Prosthet Dent. 2022;127(1):e171–3.

    Article  Google Scholar 

  38. Pantea M, Ciocoiu RC, Greabu M, Ripszky Totan A, Imre M, Țâncu AMC, Sfeatcu R, Spînu TC, Ilinca R, Petre AE. Compressive and flexural strength of 3D-printed and conventional resins designated for interim fixed dental prostheses: an in vitro comparison. Materials. 2022;15(9):3075.

    Article  PubMed  PubMed Central  Google Scholar 

  39. Digholkar S, Madhav V, Palaskar J. Evaluation of the flexural strength and microhardness of provisional crown and bridge materials fabricated by different methods. J Indian Prosthod Soc. 2016;16(4):328.

    Article  Google Scholar 

  40. Prause E, Malgaj T, Kocjan A, Beuer F, Hey J, Jevnikar P, Schmidt F. Mechanical properties of 3D-printed and milled composite resins for definitive restorations: an in vitro comparison of initial strength and fatigue behavior. J Esthet Restorat Dentist. 2023:1–11.

  41. Alzahrani SJ, Hajjaj MS, Azhari AA, Ahmed WM, Yeslam HE, Carvalho RM. Mechanical properties of three-dimensional printed provisional resin materials for crown and fixed dental prosthesis: a systematic review. Bioeng (Basel). 2023;10(6)

  42. Spagnuolo G, Sorrentino R. The role of digital devices in dentistry: clinical trends and scientific evidences. J Clin Med. 2020;9(6)

  43. Jiang T, Yan B, Jiang M, Xu B, Xu Y, Yu Y, Ma T, Wang H. Enhanced adhesion;mdash;efficient demolding integration DLP 3D printing device. Appl Sci. 2022;12(15):7373.

    Article  Google Scholar 

  44. Wang X, Liu J, Zhang Y, Kristiansen PM, Islam A, Gilchrist M, Zhang N. Advances in precision microfabrication through digital light processing: system development, material and applications. Virt Phys Protot. 2023;18(1):e2248101.

    Article  Google Scholar 

  45. Lakkala P, Munnangi SR, Bandari S, Repka M. Additive manufacturing technologies with emphasis on stereolithography 3D printing in pharmaceutical and medical applications: a review. Int J Pharmaceut: X. 2023;5:100159.

    Google Scholar 

  46. Schweiger J, Edelhoff D, Güth JF. 3D printing in digital prosthetic dentistry: an overview of recent developments in additive manufacturing. J Clin Med. 2021;10(9)

  47. Tsolakis IA, Papaioannou W, Papadopoulou E, Dalampira M, Tsolakis AI. Comparison in terms of accuracy between DLP and LCD printing Technology for Dental Model Printing. Dentist J. 2022;10(10):181.

    Article  Google Scholar 

  48. Abad-Coronel C, Pazán DP, Hidalgo L, Larriva Loyola J. Comparative analysis between 3D-printed models designed with generic and dental-specific software. Dent J. 2023;11(9):216.

    Article  Google Scholar 

  49. Moon W, Kim S, Lim BS, Park YS, Kim RJ, Chung SH. dimensional accuracy evaluation of temporary dental restorations with different 3D printing systems. Materials (Basel). 2021;14(6)

  50. Grzebieluch W, Grajzer M, Mikulewicz M. Comparative analysis of fused deposition modeling and digital light processing techniques for dimensional accuracy in clear aligner manufacturing. Med Sci Monit. 2023;29:e940922.

    Article  PubMed  PubMed Central  Google Scholar 

  51. Iftekar SF, Aabid A, Amir A, Baig M. Advancements and limitations in 3D printing materials and technologies: a critical review. Polymers. 2023;15(11):2519.

    Article  PubMed  PubMed Central  Google Scholar 

  52. Cho K, Rajan G, Farrar P, Prentice L, Prusty BG. Dental resin composites: a review on materials to product realizations. Compos Part B. 2022;230:109495.

    Article  Google Scholar 

  53. Park S, Shou W, Makatura L, Matusik W, Fu K. 3D printing of polymer composites: materials, processes, and applications. Matter. 2022;5(1):43–76.

    Article  Google Scholar 

  54. Tigmeanu CV, Ardelean LC, Rusu L-C, Negrutiu M-L. Additive manufactured polymers in dentistry, current state-of-the-art and future perspectives-a review. Polymers. 2022;14(17):3658.

    Article  PubMed  PubMed Central  Google Scholar 

  55. Al Rashid A, Ahmed W, Khalid MY, Koç M. Vat photopolymerization of polymers and polymer composites: processes and applications. Addit Manufact. 2021;47:102279.

    Article  Google Scholar 

  56. Altarazi A, Haider J, Alhotan A, Silikas N, Devlin H. Assessing the physical and mechanical properties of 3D printed acrylic material for denture base application. Dent Mater. 2022;38(12):1841–54.

    Article  PubMed  Google Scholar 

  57. Kim RJY, Kim D-H, Seo D-G. Post-polymerization of three-dimensional printing resin using a dental light curing unit. J Dent Sci. 2023. https://0-doi-org.brum.beds.ac.uk/10.1016/j.jds.2023.07.028. Epub ahead of print.

  58. Valenti C, Isabella Federici M, Masciotti F, Marinucci L, Xhimitiku I, Cianetti S, Pagano S. Mechanical properties of 3D-printed prosthetic materials compared with milled and conventional processing: A systematic review and meta-analysis of in vitro studies. J Prosthet Dent. 2022:S0022-3913(22)00415-2. https://0-doi-org.brum.beds.ac.uk/10.1016/j.prosdent.2022.06.008. Epub ahead of print.

  59. Patankar RC, More V, Jadhav R, Sabane A, Kadam P, Gachake A. Comparative evaluation of flexural strength of denture base resin materials processed using compression molding technique, injection molding technique, and computer-aided design CAM technique: an in vitro study. Dent Res J (Isfahan). 2022;19:100.

    Article  PubMed  Google Scholar 

Download references

Acknowledgments

All authors thank King Khalid University, Saudi Arabia, for the financial Support.

Funding

The authors thank the Deanship of Scientific Research at King Khalid University for funding this work through a large group Research Project under grant number RGP2/452/44.

Author information

Authors and Affiliations

  1. Department of Dental Technology, COAMS, King Khalid University, Abha, Saudi Arabia

    Ravinder S. Saini, Vishwanath Gurumurthy, Syed Altafuddin Quadri, Abdulmajeed Okshah & Abdulkhaliq Ali F. Alshadidi

  2. Department of Restorative Dental Sciences, College of Dentistry, King Khalid University, Abha, Saudi Arabia

    Shashit Shetty Bavabeedu & Khalid M. Abdelaziz

  3. Department of Therapeutic Stomatology, Faculty of Stomatology, Yerevan State Medical University after Mkhitar Heratsi, Yerevan, Armenia

    Lazar Yessayan

  4. Student Research Committee, School of Dentistry, Shiraz University of Medical Sciences, Shiraz, Iran

    Seyed Ali Mosaddad

  5. Department of Prosthodontics, Faculty of Stomatology, Yerevan State Medical University after Mkhitar Heratsi, Yerevan, Armenia

    Artak Heboyan

Authors
  1. Ravinder S. Saini
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Vishwanath Gurumurthy
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Syed Altafuddin Quadri
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Shashit Shetty Bavabeedu
    View author publications

    You can also search for this author in PubMed Google Scholar

  5. Khalid M. Abdelaziz
    View author publications

    You can also search for this author in PubMed Google Scholar

  6. Abdulmajeed Okshah
    View author publications

    You can also search for this author in PubMed Google Scholar

  7. Abdulkhaliq Ali F. Alshadidi
    View author publications

    You can also search for this author in PubMed Google Scholar

  8. Lazar Yessayan
    View author publications

    You can also search for this author in PubMed Google Scholar

  9. Seyed Ali Mosaddad
    View author publications

    You can also search for this author in PubMed Google Scholar

  10. Artak Heboyan
    View author publications

    You can also search for this author in PubMed Google Scholar

Contributions

Conceptualization and Methodology: Ravinder Saini, Vishwanath Gurumurthy. Data Curation and Formal Analysis: Shashit Bavabeedu, Khaled Abdelaziz, Seyed Ali Mosaddad. Investigation and Resources: Abdulmajeed Okshah, Syed Altafuddin. Original draft preparation: Ravinder S Saini, Artak Heboyan, Abdulkhaliq Alshadidi, Lazar Yessayan. Writing, Reviewing and Editing: Shashit Bavabeedu, Khaled Abdelaziz, Abdulmajeed Okshah, Seyed Ali Mosaddad. Supervision and Project Administration: Abdul Khaliq, Artak Heboyan, Lazar Yessayan. Funding Acquisition: Abdul Khaliq.

Corresponding authors

Correspondence to Seyed Ali Mosaddad or Artak Heboyan.

Ethics declarations

Ethics approval and consent to participate

Not applicable.

Consent for publication

Not applicable.

Competing interests

The authors declare no competing interests.

Additional information

Publisher’s Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary Information

Additional file 1:  Appendix 1.

List of Items (CONSORT Scale).

Additional file 2: Supplementary Table 1.

Literature search strategy.

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/. The Creative Commons Public Domain Dedication waiver (http://creativecommons.org/publicdomain/zero/1.0/) applies to the data made available in this article, unless otherwise stated in a credit line to the data.

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Saini, R.S., Gurumurthy, V., Quadri, S.A. et al. The flexural strength of 3D-printed provisional restorations fabricated with different resins: a systematic review and meta-analysis. BMC Oral Health 24, 66 (2024). https://0-doi-org.brum.beds.ac.uk/10.1186/s12903-023-03826-x

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI: https://0-doi-org.brum.beds.ac.uk/10.1186/s12903-023-03826-x

Keywords

BMC Oral Health

ISSN: 1472-6831

Contact us